High hoop-stress pipe

ABSTRACT

Pipe formed from high-density high-molecular weight poly(1monoolefin) compositions containing small amounts of graphite exhibits high hoop-stress life. In addition, the compositions can contain carbon black and a slip agent.

United States Patent [191 Carrow 1 Sept. 2, 1975 l" HIGH HOOP-STRESS PIPE [75] Inventor: Guy E. Carrow, Bartlesville, Okla.

[73] Assignee: Phillips Petroleum Company,

Bartlesville, Okla.

[22] Filed: July 8, 1974 [21] Appl. No.: 486,684

Related US. Application Data [63] Continuation-impart of Ser. No. 234,317. Mar. 13.

[52] US. Cl. 138/177; l38/DIG. 7; 161/139; 161/247; 161/411; 252/511; 260/41 R [51] Int. Cl. Fl6l 9/12; C08f 45/08 [58] Field of Search 138/177, 178, DIG. 7; 260/41 R; 252/510, 511; 161/247,.139, 411

[56] References Cited UNITED STATES PATENTS 4/1943 Mueller-Cunradi et a1. 260/42.46 1/1965 Dixon 252/510 3,206,419 9/1965 Pritchard et a1. 260/29.] R

3,455,865 7/1969 Bolt et all. 1 17/6 3,492,310 1/1970 Car-row 260/33.4 3,703,565 11/1972 I-Ioblit et al. 260/878 B FOREIGN PATENTS OR APPLICATIONS 1,044,503 10/1966 United Kingdom OTHER PUBLICATIONS Encyclopedia of Polymer Science and Technology, Vol. 6, John Wiley & Sons, 1967, pp. 358-362.

Primary Examiner-Richard E. Aegerter Assislanl ExaminerL. Footland 13 Claims, No Drawings 1 HIGH HOOP-STRESS PIPE RELATED INVENTION is application is a continuation-in-part application oi copending application having Ser. No. 234,317, filed Mar. 13, 1972, now allowed.

FIELD OF THE INVENTION This invention relates to high molecular weight poly- (1-monoolef1n)-graphite compositions. This invention further relates to pipe exhibiting high hoop-stress properties.

BRIEF SUMMARY OF THE INVENTION According to my invention, there are provided compositions of high molecular weight high density poly( 1- monoolefin)s blended or compounded with graphite.

Extruded hollow forms, particularly substantially rigid tubular forms such as pipe, prepared from these graphite-containing high density high molecular weight poly( l-monoolefin)s compositions exhibit unexpectedly high hoop-stress life by considerable margins as compared to pipe prepared from poly( l-monoolefin)s not containing the graphite.

DETAILED DESCRIPTION OF THE INVENTION I have discovered that unique compositions of a minor amount of graphite and a major amount of high density poly( l-monoolefin)s, more particularly the extra-high molecular weight polymers characterized by a high load melt index below about 5 but not less than 0.1, such as high density, high molecular weight polyethylene, can be shaped or extruded into various substantially rigid tubular forms such as pipe which exhibit surprisingly high hoop-stress life.

Polymers Broadly, the polymers useful in the context of my invention are high molecular weight polymers of l monoolefins. These poly(l-monoolefin)s include homopolymers or copolymers of l-monoolefins containing from 2 to 12, presently preferably 2 to 6 for commercial availability, carbon atoms per molecule, such as ethylene, propylene, butylene, pentene, hexene, cyclooctene, octene, dodecene, or polymerizable skeletal isomers thereof. These monomers can be polymerized as homopolymers of any one monomer, copolymers of any two or three or more, and the like, such as the pres ently preferred ethylene homopolymers, ethylenebutene copolymers, and ethylene-hexene copolymers.

The high molecular weight high density poly( 1- monoolefin)s can be prepared by means known to the polymer arts using a supported metal oxide catalyst, such as chromium oxide; or by the use of transition metal halides and organo-metal compound catalysts; or other methods known in the art.

In general, the high molecular weight high density polymers which presently are considered most suitable for my invention are those high molecular weight polymers of lolefms with a high load melt index (HLMI) below 5 but not less than about 0.1, preferably at least about 0.5, more preferably about 1 to 5, as determined by ASTM Method D l238-65T Condition F.

It is presently preferred that the molecular weight of the poly( l-monoolefin)s, as determined by gel permeation chromotography, be within the broad range of 200,000 to 1,000,000, more preferably 250,000 to 800,000, still more preferably from 300,000 to 2 500,000, as measured by methods known to the arts such as on Waters Associates, Inc. Instruments. The presently preferred polymers have a density of about 0.94 to 0.97 by ASTM Method D 1505-68. Graphite According to said copending application, the graphite contentof the poly( l-monoolefin)-graphite compositions of my invention range broadly from about 1 to 10 weight percent relative to the weight of poly(lmonoolefin) alone, excluding weight of other additives incorporated into the composition for various pur' poses, as well as fillers, colorants, and the like. Presently preferred for commercial purposes, according to said copending application, are compositions contain ing a graphite content of about 2 to 6 percent by weight on the same basis.

In accordance with the invention, it has now been found that tubular form pipe exhibiting high hoopstress life when subjected to a hoopstress of at least 1,000 pounds and a temperature of about I50F can be prepared from high molecular weight high density poly olefins containing 0.5 to 3 weight percent graphite. It has been further found that high molecular weight high density polyolefin compositions containing small amounts of graphite and like amounts of carbon black can be formed into tubular pipe exhibiting high hoopstress life.

As is demonstrated by the specific working examples hereinbelow, polyolefin compositions, especially polyethylene, ethylene-butene copolymers, and ethylenehexene copolymers, containing 0.5 to 3 weight percent graphite or such compositions also containing 1 to 3 weight percent carbon black can be shaped or extruded into rigid tubular form such as pipe which exhibits surprisingly high hoop-stress life in comparison with pipe formed from polyolefin compositions containing only carbon black. Moreover, as demonstrated by the specific working examples, particularly effective polyolefin compositions containing both graphite and carbon black are obtained for the formation of pipe having excellent high hoop-stress properties when the total content of carbon black and graphite together did not exceed about 4 weight percent relative to the weight of the polymer resin itself.

Graphite, sometimes termed black lead or plumbago, commonly is described as a crystalline allotropic form of carbon characterized by hexagonal arrangement of atoms. Graphite also is produced synthetically from petroleum coke and sometimes is known as pyrographite or pyrolytic graphite. Commerically available are various graphite forms including crystalline types, the pyrolytic type, and also an amorphous form from some areas in the world.

Graphite can be incorporated into the described high melt index polymers by such means as a compounding extruder and pelletizer, Banbury mixer, or other equipment for compounding additives into thermoplastic materials. Preferred is a finely divided or powdered graphite. The graphite can be added for convenience at the same time as are other additives such as antioxidants, colorants, stabilizers, and the like.

Other Additives Various other additives can be used to impart other desirable properties to the polymeric compositions of this invention, such as improving oxidative stability, light stability, weatherability, or to add fungicides, corrosion inhibitors, and the like. Various additives also can be added including fillers, colorants, and the like,

3 and including, particularly for preparataion of pipe, the use of carbon black such as to the extent of about 0.5 to 8 weight percent, preferably 1 to weight percent, based on the weight of polymer excluding other additives.

In general, as set forth in said copending application, presently preferred for commercial purposes are compositions ofpoly(1-monoolef1n)s wherein the total content of carbon black and graphite together does not exceed about weight percent relative to the weight of the polymer resin itself. As demonstrated by the working examples below, currently preferred are compositions of polyolefins such as polyethylene, ethylenebutene copolymers, and ethylene-hexene copolymers wherein the total content of carbon black and graphite together does not exceed about 4 weight percent relative to the weight of the polymer resin itself.

Various processing aids can be incorporated into the resin for various purposes. Particularly desirable for dynamic extrusion purposes are slip agents such as glycerin or an amide of a higher fatty acid, or both, to improve extrusion properties.

High molecular weight high density po1y( 1- monoo1efin)s, while tough, require specialized processing techniques such as the use of dynamic extruders. Frequently, glycerin or amides, or both, are added as slip agents to the raw resin, or to the resin compounded with carbon black or the like. The amides of saturated and/or unsaturated substantially water insoluble aliphatic monocarboxylic acids are useful such as those of 4 intended illustrative of my invention and not limitedly of the reasonable scope thereof.

To illustrate the unusual nature and highly desirable properties of my compositions, pipe was formed from my compositions and also from control compositions for comparison, by dynamic extrusion, a process of extrusion utilizing repeated pressure impulses and a long land die. Such methods of extrusion are particularly helpful in extruding high density, high molecular weight poly(1-monoolefin)s.

EXAMPLE I An ethylene-butene-l copolymer, density 0.942, high load melt index 1 (ASTM D 1238-65T Condition F), molecular weight as determined by gel permeation chromotography of about 400,000, was compounded with 0.1 percent by weight of a known stabilizer 4,4- thiobis(6-tert-m-cresol), 0.8 weight percent glycerol, and 2.5 weight percent of a 200 mesh graphite powder in a Banbury mixer. The control runs were prepared similarly, using the same polymer, but employing 2.5 weight percent carbon black rather than graphite. Each composition was comminuted by a chopper into granules.

One-inch schedule pipe then was extruded. Sections of pipe prepared from the compositions were subjected to long-term hoop-stress testing according to ASTM Method D 1598-58T. The results are tabulated below and compared with standard pipe samples from 30 production line resin without the added graphite:

TABLE I Hoop Hours to Failure of Pipe Weight Additive Stress, Under Long-Term Hoop 1000 Hoop Stress a out 225 psig internal pressure. Runs 2A, 4A. 6A. and 8A were made with the polymer described in Example 11 which differs slightly from the polymer of Example 1. but is considered equivalent.

acids having from 10 to 22 carbon atoms in the molecule such as are present as free acids or glycerides in fatty oils. Typical fatty acid amides include the amides of lauric acid, myristic acid, palmitic acid, stearic acid, oleic acid, and linoleic acid, alone or in admixture.

The amount of glycerine used ranges from about 0.5 to 1.5 percent by weight of the extrusion composition. An amide can be added in an amount ranging from about 0.1 to 1 percent by weight of the extrusion composition. The glycerine and amide can be incorporated by dry blending, that is, by mixing the additives with the granular or pelleted resin, for example, as by tumbling or by precompounding in a Banbury mixer or a Farrow continuous mixer, and the like.

EXAMPLES Materials used in the following examples, proportions, particular specific components, and the like, are

The above data fully illustrate the unexpectedly improved nature of my polyolefin-graphite compositions.

EXAMPLE 11 TABLE 11- Additive to t Polyethylene Short-Time* t Hours to Failure of Pipe Pipc Wt. Percent Rupture UndcrLong-Term Sample Carbon Strength, Hoop-Stress, lb/in-'** & 150 F No, Black Graphite lb/ll'l 1200 5 1100 1000* 900 900 failure) 3 1.5 1.0 800 65.0 1752 5064 2569 4392 4 2.0 1,0 800 105.7" 552" 6648 2208 4464 5 2,0 1.0 800 13.5" 3552 13048 10363 6 0 2.5 780 87.9 6360 12936 16896 16248 ASTM 134598583.

"1000 lb, Hoop stress about 225 psig internal pressure. t

"Failed near the fitting apparently the pipe was weakened while it was put on test. Equivalent Sample 5 behaves as expected. Samples 4 and 5 had the same composition and at 1200 psi 5 failed early while the other (4) was much better.

Referring to the above table, it can be seen that all taining 0.5 weight percent graphite gave better results blends had very nearly the same short-time rupture than the compounded 0.5 weight percent blend of Run strength. In addition, while not every long-term stress 3. As can be seen from the data'in Table III, as little as test in the table was consistent, overall the blends con- 0.5 weight percent graphite has a beneficial effect taining graphite were better than Run 1 containing only when compounded with polyolefins containing carbon carbon black. It will also be observed that Run 6 conblack which are formed into pipe exhibiting high hooptaining graphite only was excellent at all test pressures stress life. below 1200 psi. In general, based upon the data above, Variations and modifications of my invention can be the blends containing graphite exhibited high hoopmade, as will be apparent to one skilled in the art, yet stress life when subjected to a hoop-stress of at least without parting from the intended spirit and scope of 1000 pounds. my disclosure including the claims as here appended.

I-claim: 1 EXAMPLE 1. A tubular form pipe exhibiting high hoop-stress life A high molecular weight high density ethylenewhen subjected to a hoop stress of at least 1000 pounds butene-l copolymer, density 0.941, high load melt and a temperature of about 150F prepared from a comindex 1.0, molecular weight about 400,000, was composition consisting essentially of at least one high mo pounded with 0.9 weight percent glycerine and 2.5 lecular weight high density poly(1monoolefin) seweight percent carbon black and varying amounts of 3 lected from homopolymers and copolymers of 1- graphite ranging from 0.5 weight percent to one weight monoolefins having from 2 to 12 carbon atoms per percent. molecule and graphite, said poly( l-monoolefin) being One-inch schedule 40 pipe was extruded from the characterized by a high load melt index of less than 5 polyethylene resin. Sections of pipe prepared from the but not less than 0.1, said graphite being present to the compositions were subjected to long-term hoop-stress 4Q extent of about 0.5 to about 3 weight percent relative testing according to ASTM D 1598-58T. The results to the weight of said poly(l-monoolefin).

are tabulated below in Table 111: 2. A tubular form pipe as defined in claim 1 wherein TABLE 111 Hours to Failure of Pipe Pipe Additive Concentration Under Long-Term Hoop- Sample Wt.% Stress & 15OF No. Carbon Black Graphite 1050 psi Stress 1000 psi Stress l 2.5 1 2160 (average) 3600 (no failure) 2 2.5 1 2928 2928 (no failure) 3 2.5 0.5 1904 (average) 2288 (average) 4 2.5 0.5* 2840 (average) 6534 (average) 5 2.5 0 2280 5050 blend of resin containing 1 percent by weight graphite and resin containing no graphite. "1000-lb. hoop stress 225 to 230 psig internal pressure.

In the above table values indicated as being average said high molecular weight, high density poly(1- are average values obtained for three runs. It will also monoolefin) is further characterized by a molecular be noted that Samples 1 and 2 subjected to 1000 psi weight of 200,000 to 1,000,000, a density of 0.94 to stress and Sample 2 subjected to 1050 psi stress did not 0.97, and a high load melt index of 0.5 to 5.

fall and tests were terminated after the indicated lapse 3. The pipe defined by claim 11 further containing of time. from about 0.5 to about 8 weight percent of carbon Run 5 in Table III corresponds to Run 1 in Table 11. black relative to the weight of said poly( l-monoolefin) Both resins are the same polymer but different producwherein the total content of said graphite and of said tion lots. carbon black together do not exceed about 10 weight The data in Table III demonstrate that pipe containpercent relative to the weight of said poly( 1- ing one percent by weight graphite and 2.5 weight permonoolefin). cent carbon black is considerably better than pipe con- 4. The pipe defined by claim 1 further containing taining no graphite at 1000 psi stress. It will also be about 1 to about 3 weight percent carbon black and noted that Run 4 which is a physical 5050 blend conwherein the total content of said graphite and of said carbon black together do not exceed about 4 weight percent relative to the weight of said poly( lmonoolefin).

5. The pipe defined by claim 1 further containing 1 to 3 weight percent carbon black and a slip agent wherein said slip agent is glycerine, an amide of a higher fatty acid, or both, and wherein the amount of glycerine present is 0.5 to 1.5 weight percent and the amount of amide present is 0.1 to 1 weight percent.

6. A pipe defined by claim 1 further incorporating a slip agent, said slip agent is a glycerol, an amide of a higher fatty acid, or both, and wherein the amount of glycerin present is 0.5 to 1.5 weight percent and the amount of amide present is 0.1 to l weight percent.

7. The pipe defined by claim I wherein said poly( lmonoolefin) is polyethylene, an ethylene-butene copolymer, or an ethylene-hexene copolymer.

8. The pipe defined by claim 1 wherein said poly( l-.

8 weight percent, and the amount of amide present is 0.1 to 1 weight percent.

10. A tubular form pipe exhibiting high hoop-stress life prepared from a high molecular weight high density poly( l-monoolefin) selected from the group consisting of polyethylene and ethylene-butene copolymers containing up to 10 weight percent butene and about 2.5 weight percent graphite relative to the weight of said poly( l-monoolefin), said poly( l-monoolefin) being characterized by a high load melt index of 0.5 to 5, a molecular weight of 200,000 to 1,000,000, and a density of 0.94 to 0.97.

11. The pipe defined by claim 10 further containing from 0.5 to 8 weight percent of carbon black relative to the weight of said poly( l-monoolefin) and wherein the total content of said graphite and of said carbon black together do not exceed about 10 weight percent relative to the weight of said poly( l-monoolefin).

12. A pipe defined by claim 10 further containing a slip agent wherein said slip agent is glycerine, an amide of a higher fatty acid, or both, and wherein the amount of glycerine present is 0.5 to 1.5 weight percent, and the amount of amide present is 0.1 to 1 weight percent.

13. The pipe defined by claim 10 further containing 1 to 5 weight percent carbon black and 0.5 to 1.5

weight percent glycerine. 

1. A TUBULAR FORM PIPE EXHIBITING HIGH HOOP-STRESS LIFE WHEN SUBJECTED TO A HOOP STRESS OF AT LEAST 1000 POUNDS AND A TEMPERATURE OF ABOUT 150*F PREPARED FROM A COMPOSITION CONSISTING ESSENTIALLY OF AT LEAST ONE HIGH MOLECULAR WEIGHT HIGH DENIST POLY(1-MMONOOLEFIN) SELECTED FROM HOMOPOLYMERS AND COPOLYMERS OF 1-MONOOLEFINS HAVING FROM 2 TO 12 CARBON ATOMS PER MOLECULE AND GRAPHITE, SAID POLY(1-MONOOLEFIN) BEING CHARACTERIZED BY A HIGH LOAD MELT INDEX OF LESS THAN 5 BUT NOT LESS THAN 0.1, SAID GRAPHITE BEING PRESENT TO THE EXTENT OF ABOUT 0.5 TO ABOUT 3 WEIGHT PERCENT RELATIVE TO THE WEIGHT. OF SAID POLY(1-MONOOLEFIN).
 2. A tubular form pipe as defined in claim 1 wherein said high molecular weight, high density poly(1-monoolefin) is further characterized by a molecular weight of 200,000 to 1,000,000, a density of 0.94 to 0.97, and a high load melt index of 0.5 to
 5. 3. The pipe defined by claim 1 further containing from about 0.5 to about 8 weight percent of carbon black relative to the weight of said poly(1-monoolefin) wherein the total content of said graphite and of said carbon black together do not exceed about 10 weight percent relative to the weight of said poly(1-monoolefin).
 4. The pipe defined by claim 1 further containing about 1 to about 3 weight percent carbon black and wherein the total content of said graphite and of said carbon black together do not exceed about 4 weight percent relative to the weight of said poly(1-monoolefin).
 5. The pipe defined by claim 1 further containing 1 to 3 weight percent carbon black and a slip agent wherein said slip agent is glycerine, an amide of a higher fatty acid, or both, and wherein the amount of glycerIne present is 0.5 to 1.5 weight percent and the amount of amide present is 0.1 to 1 weight percent.
 6. A pipe defined by claim 1 further incorporating a slip agent, said slip agent is a glycerol, an amide of a higher fatty acid, or both, and wherein the amount of glycerin present is 0.5 to 1.5 weight percent and the amount of amide present is 0.1 to 1 weight percent.
 7. The pipe defined by claim 1 wherein said poly(1-monoolefin) is polyethylene, an ethylene-butene copolymer, or an ethylene-hexene copolymer.
 8. The pipe defined by claim 1 wherein said poly(1-monoolefin) is an ethylene-butene copolymer containing 2.5 weight percent graphite and 0.8 weight percent glycerol.
 9. The pipe defined by claim 1 wherein said polyolefin is polyethylene, an ethylene-butene copolymer or an ethylenehexene copolymer, and further wherein said compositions contain from 1 to 3 weight percent carbon black and a slip agent wherein said slip agent is glycerine, an amide of a higher fatty acid, or both, and wherein the amount of glycerine present is 0.5 to 1.5 weight percent, and the amount of amide present is 0.1 to 1 weight percent.
 10. A tubular form pipe exhibiting high hoop-stress life prepared from a high molecular weight high density poly(1-monoolefin) selected from the group consisting of polyethylene and ethylene-butene copolymers containing up to 10 weight percent butene and about 2.5 weight percent graphite relative to the weight of said poly(1-monoolefin), said poly(1-monoolefin) being characterized by a high load melt index of 0.5 to 5, a molecular weight of 200,000 to 1,000,000, and a density of 0.94 to 0.97.
 11. The pipe defined by claim 10 further containing from 0.5 to 8 weight percent of carbon black relative to the weight of said poly(1-monoolefin) and wherein the total content of said graphite and of said carbon black together do not exceed about 10 weight percent relative to the weight of said poly(1-monoolefin).
 12. A pipe defined by claim 10 further containing a slip agent wherein said slip agent is glycerine, an amide of a higher fatty acid, or both, and wherein the amount of glycerine present is 0.5 to 1.5 weight percent, and the amount of amide present is 0.1 to 1 weight percent.
 13. The pipe defined by claim 10 further containing 1 to 5 weight percent carbon black and 0.5 to 1.5 weight percent glycerine. 